Corrosion Behavior of Bare, Cr3C2-25%(NiCr), and Cr3C2-25%(NiCr)+0.4%CeO2-Coated Superni 600 Under Molten Salt at 900 °C
Crossref DOI link: https://doi.org/10.1007/s11665-014-1177-3
Published Online: 2014-08-05
Published Print: 2014-11
Update policy: https://doi.org/10.1007/springer_crossmark_policy
Mudgal, Deepa
Kumar, Sanjeet
Singh, Surendra
Prakash, Satya